On July 9, 2001, about 1725 eastern daylight time, a Hughes 269A, N7028V, was substantially damaged when it rolled over during a precautionary landing near Clay, New York. The certificated commercial pilot and passenger received minor injuries. Visual meteorological conditions prevailed for the personal flight that originated from the Oswego County Airport (FZY), Fulton, New York, destined for the Hancock International Airport (SYR), Syracuse, New York. A flight plan was not filed, and the flight was conducted under 14 CFR Part 91. According to the pilot, he was in cruise flight when he heard a "bang." He then advised Syracuse Air Traffic Control Tower that he was making a precautionary landing. The pilot identified an area, and turned the helicopter 180 degrees to maneuver for his anticipated landing point. During the turn, the pilot looked back at the tailrotor and saw that it was still rotating, but he did not have tailrotor authority. The pilot lowered the collective and started a descent. He then started to reduce the airspeed in anticipation of landing. The helicopter began to rotate, and 30 to 50 feet agl, the pilot pulled collective to cushion the "fall." The helicopter impacted the ground and rolled onto its left side. The pilot and passenger then egressed. According to a Federal Aviation Administration inspector, initial examination of the left tailboom support cluster fitting revealed that the left tailboom attaching point had separated, and the fracture surfaces were dark in color. The tailrotor drive shaft was severed where it entered the aft portion of the fuselage. Both sections of the shaft displayed rotational scoring. According to maintenance records, the helicopter received an annual inspection on July 26, 2000, 23.3 flight hours prior to the accident. During the annual inspection, the mechanic documented that he preformed the requirements of airworthiness directive (AD) 76-18-01 According to a factual report generated by the Safety Board's Materials Laboratory, portions of the fracture surfaces for the cluster fitting lugs were relatively flat with smooth curving boundaries, "features typical of fatigue." Most of the relatively rough area in the lower lug had curving arrest lines, "features typical of low-cycle fatigue." According to AD 76-18-01, within 50 flight hours of the effective date of the AD, and thereafter at intervals not to exceed 50 hours of flight time, or until modifications were accomplished, the cluster fittings were to be visually inspected for deformation or damage, and then checked for cracking using dye penetrant. If cracking or damage was identified, the effected structure would have had to be replaced. The AD also required the dye penetrant inspection be done in accordance with Service Information Notice N-82.3, which stated that the paint be removed from the fitting prior to the inspection. If the fitting was serviceable, a wash coat of zinc chromate primer, and then a coat of epoxy enamel would have had to been applied. In addition, the Service Information Notice stated that a daily visual inspection was required. According to the mechanic, he inspected the cluster fitting in accordance with the AD and the Information Service Notice when he preformed the annual inspection. In addition, the pilot stated that he performed a visual inspection of the aft clevis lugs prior to the first flight of the day, to include the accident flight.