HISTORY OF FLIGHT On December 5, 2004, about 1400 Alaska standard time, a Boeing 747SR-146B SF airplane, Japanese registration JA8158, sustained minor damage during a rapid decompression event while in normal cruise flight, about 137 miles west of Anchorage, Alaska. The airplane was being operated as Flight KZ103, by Nippon Cargo Airlines of Tokyo, Japan, as an instrument flight rules (IFR) non-scheduled international cargo flight under Title 14, CFR Part 129, when the incident occurred. The three flight crew members were not injured. Visual meteorological conditions prevailed, and an instrument flight plan was filed. The flight originated at the Ted Stevens International Airport, Anchorage, about 1338, and was bound for the Narita International Airport, Tokyo, Japan. Upon reaching an altitude of 30,000 feet the airplane had a rapid decompression, and returned to the Ted Stevens International Airport. During a telephone conversation with the National Transportation Safety Board (NTSB) investigator-in-charge (IIC) on December 5, the FAA aviation safety inspector who examined the airplane said he saw a 12-inch elliptical tear in the right side of the pressure bulkhead web separating the electronics service bay from the nose wheel well. During an examination of the airplane by the IIC on December 7, a rupture of the right side pressure bulkhead web inside the nose wheel well was seen. The tear extended about 12-inches along a horizontal rivet line. Both ends of the torn skin turned downward approximately 80-90 degrees, and the skin was bent outward 90 degrees to the bulkhead. No other damage resulting from the rupture was seen. The damaged area (STA 260-280, WL 160-170) was excised from the structure by a team from Boeing, and delivered to the IIC. AIRCRAFT INFORMATION The accident airplane is a Boeing 747-100SR (cargo configuration), serial number 22711. At the time of the incident the airplane had logged 58,185 flight hours, and 27,243 cycles/landings. TEST AND RESEARCH On January 19, the excised material was hand-delivered to the Boeing Material and Process Technology Fracture Analysis Group, Seattle, Washington. Under the supervision of the NTSB, a detailed examination of the fracture mechanism was conducted. The fracture exam concluded that the web fracture was initiated by fatigue from multiple origins on the outboard surface within the pressure vessel. A total of 10 separate fatigue cracks, ranging from 0.48 to 0.94 inch in width, propagated through the full web thickness, before the onset of rapid ductile tearing. Each fatigue crack formed adjacent to a fastener hole common with the WL 170 beam. The cracking was in line with the edge of the bonded strip doublers on the inboard surface (wheel well side). Metallurgical analysis showed the material met all the engineering drawing requirements. A copy of the fracture examination is attached to the docket for this case. OTHER INFORMATION Inspection criteria for the affected area is contained in Boeing Service Bulletin 747-53A24645 (April 5, 2001), and Alert Revisions 1 thru 4. Information gathered during the material analysis of this incident investigation was instrumental in the creation/adoption of Alert Revision 4 (February 24, 2005). Alert Revision 4 adds the requirement for repeated inspections of areas 1 and 2, at 500 flight-cycle intervals once the airplane has reached 20,000 flight cycles. It also decreased the inspection intervals of area 3 from 6,000 flight-cycles to 1,500 flight-cycles.