HISTORY OF FLIGHTOn April 4, 2019, about 1416 eastern daylight time, a Robinson R44 II helicopter, N4046J, was substantially damaged during a forced landing to a roadway near Tampa, Florida. The pilot and the passenger were not injured, but a passenger in a nearby vehicle was fatally injured, and the driver of the vehicle sustained serious injuries. Visual meteorological conditions prevailed, and no flight plan was filed for the positioning flight, which was destined for Sarasota/Bradenton International Airport (SRQ), Sarasota, Florida. The positioning flight was conducted under the provisions of Title 14 Code of Federal Regulations Part 91. The owner of the helicopter reported that, 5 days before the accident, he had flown the helicopter for about 1 hour at an altitude of 1,000 ft mean sea level when the engine lost total power. He located a field for landing and performed an autorotation to the ground. The helicopter was not damaged during the landing. The owner further stated that he restarted the engine and that it ran at idle for several minutes before he pulled on the collective and the engine lost power again. The owner restarted the engine and kept the main rotor disengaged while he ran the engine up to 100% power without a load; the owner reported that the engine ran well but that, when he engaged the main rotor and started to pull on the collective, the engine lost power another time. The owner shut down the engine and contacted the helicopter manufacturer about repairing the helicopter. A Federal Aviation Administration (FAA) inspector contacted the pilot on the morning of the accident and told him that work on the helicopter was being performed by two mechanics from Florida Suncoast Helicopters. According to the FAA inspector, he observed the Florida Suncoast Helicopters mechanics as they performed maintenance on the helicopter in the field where the helicopter had previously landed. The mechanics told the inspector that they had cleaned the fuel screen and looked for contamination. A pilot employed by Florida Suncoast Helicopters then started the engine and let it warm up. The pilot subsequently pulled on the collective, and the engine lost total power. After discussion with the helicopter manufacturer, the mechanics replaced the fuel servo unit with a new one. The FAA inspector then departed and asked the mechanics to call after the repairs were complete, and to tell him what was repaired. According to the mechanics and the pilot employed by Florida Suncoast Helicopters, after the fuel servo unit was changed, the pilot performed a test run of the engine and hovered the helicopter for several minutes. No problems were noted. The pilot and one of the mechanics boarded the helicopter and departed the field about 1401 with the intent of repositioning the helicopter to SRQ, where the company's maintenance facility was located. About 15 minutes later, the engine lost total power, and the pilot performed an autorotation to a roadway. After touchdown on the roadway, the helicopter slid on the pavement due to its forward momentum. The helicopter then slid sideways, and the main rotor blades contacted a telephone pole, and a 2.5-ft-long piece of a main rotor blade separated and impact the windshield of a truck driving on the roadway. PERSONNEL INFORMATIONThe pilot held a commercial pilot certificate with a rating for rotorcraft-helicopter. He held an FAA-issued second-class medical certificate, dated March 20, 2019. According to the pilot's logbook, he had a total of 657.9 hours of flight experience. AIRCRAFT INFORMATIONThe four-seat helicopter was manufactured in 2019. It was powered by a Lycoming IO-540-AE1A5, 260-horsepower engine. At the time of the accident, the airframe and engine total time was 81.34 hours. AIRPORT INFORMATIONThe four-seat helicopter was manufactured in 2019. It was powered by a Lycoming IO-540-AE1A5, 260-horsepower engine. At the time of the accident, the airframe and engine total time was 81.34 hours. WRECKAGE AND IMPACT INFORMATIONThe helicopter came to rest along a heading of 180 next to a telephone pole that had been cut in half. Both main rotor blades were fractured at the tips and had cable cuts along the blades. The skids on the helicopter were damaged, consistent with a hard landing, and the skids' rear cross- tube was fractured. The tailcone was buckled on the top located at the second bay. One pitch link for the rotor blade had fractured and separated. The vertical firewall was wrinkled at the lower right corner. Examination of the engine revealed that the induction air inlet duct was partially collapsed. The inner rubberized fabric liner of the duct had partially delaminated and separated from the outer rubberized fabric, obstructing the interior volume of the duct. The wire stiffener between the two layers of fabric was displaced in two locations near the center of the duct length, at the 90° bend. No other discrepancies of the airframe or engine were noted. The induction air inlet duct was provided to the National Transportation Safety Board's Materials Laboratory for further investigation. The duct was dissected to examine the internal surfaces. A liquid residue was observed in some areas of the duct. The residue was analyzed, and the best matches were several oxidized vegetable oils, including castor oil, which was used by the duct manufacturer, along with a water-based release agent, in the assembly and curing of the air inlet duct. ADDITIONAL INFORMATIONConstruction of the Duct The helicopter engine's induction air inlet duct consisted of a tube section with an inner layer made from fiberglass cloth that was impregnated with a silicone rubber. A corrosion-resistant steel wire was wound in a helix over the top of the inner layer and an outer layer of rubberized silicone cloth was wrapped over the top of the wire, thereby embedding the wire in between two layers of rubberized cloth. Two fiberglass cords were then wrapped around the outside of the tube, one cord on either side of the helical steel wire. Each end of the duct was terminated by a rubberized fiberglass cloth cuff. The duct was manufactured by using partially-cured sheets of rubberized cloth and assembling the tube components on a mandrel. The assembled tube was then cured in an oven, thereby co-curing the inner and outer layers. Post-Accident Safety Actions As a result of this accident, Robinson Helicopter issued Service Bulletin (SB)-97, dated April 11, 2019, pertaining to the inspection of air induction hoses with part No. A785-31 on specific R44 II helicopters. The SB advised R44 II helicopter owners, operators, and maintenance personnel to, within 1 flight hour, "visually inspect inside of hose to verify no separation between outer and inner layers." The SB also advised "flex the hose and listen for a crinkling sound, which is an indication of separation" and "prior to further flight, replace any hose with an indication of separation." Robinson Helicopter also issued SB-100, dated July 3, 2019, expanding the inspections to other R44 II helicopters and spare A785-31 air induction hoses that shipped through March 2019. The FAA issued Airworthiness Directive 2019-12-18, effective July 5, 2019, requiring inspection of the air induction hose, within 10 hours time in service, on specific R44 II helicopters, including those with an A785-31 hose installed after April 30, 2018. The airworthiness directive indicated that, "if there is any separation or crinkling sound, replace the hose before further flight"; otherwise, the hose could be replaced within 50 hours time in service.